10Cr17Ni13Mo2Ti stainless 316Ti Seamless Stainless Steel Pipes as GOST9941
Materials:10Cr17Ni13Mo2Ti ,316Ti,08Cr18Ni10Ti,TP321,F321,TP304,TP316,TP316L
Application:For Stainless boiler tubes,pressure line stainless pipes.
1. Commodity: 10Cr17Ni13Mo2Ti stainless 316Ti Seamless Stainless Steel Pipes as GOST9941
2. Process method: seamless cold and warm-deformed stainless tubes
3. Surface finish: annealing, pickling and polishing as required
4. Material Grades: 08Cr18Ni10Ti,TP321,F321,TP304,TP316,TP316L
5. Specifications: ASTM A789,ASME SA/A789, SA/A790, EN10216-5, etc.
6. Size:
A) NPS: 1/8" to 6"
B) Schedule: 10S, 40/40S, 80/80S, 120, 160, XS, XXS
C) O. D.: 6 mm to 500 mm
D) W. T.: 0.5 mm to 30 mm
E) Length: Max. 25 meters
7.Packaging: seaworthy wooden case/steel framed plywood case/bundles packaging depending on products,
destination,method of shipment and client requirement
8. Certificate: ISO 9001:2008, PED ASME,Materials certificate as EN10204.3.1B
Chemical compostion of 08Cr18Ni10Ti stainless steel pipes:
About the other stainless steel pipes that we are suppling:
| Stainless Steel Mechanical Properties | ||||||
| Grade | Tensile Strength | Yide Strength | Elogation | Hardness | Solution Annealing | |
| kgf/mm²(N/mm²) | kgf/mm²(N/mm²) | % | HRB(HV) | ºC | ||
| ASTM | TP 304 | ≥53 (515) | ≥21 (205) | ≥35 | ≤90 (200) | 1040ºC-1150ºC Water Quenching |
| TP 304L | ≥50 (485) | ≥17 (170) | ||||
| TP 316 | ≥53 (515) | ≥21 (205) | ||||
| TP 316L | ≥50 (485) | ≥17 (170) | ||||
| JIS | SUS 304 | ≥53 (520) | ≥21 (205) | 1010ºC-1150ºC Water Quenching | ||
| SUS 304L | ≥49 (480) | ≥18 (175) | ||||
| SUS 316 | ≥53 (520) | ≥21 (205) | ||||
| SUS 316L | ≥49 (480) | ≥18 (175) | ||||
| GB | 06Cr19Ni10 | ≥53 (520) | ≥21 (210) | 1010ºC-1150ºC Water Quenching | ||
| 022Cr19Ni10 | ≥49 (480) | ≥18 (180) | ||||
| 06Cr17Ni12Mo2 | ≥53 (520) | ≥21 (210) | ||||
| 022Cr17Ni12Mo2 | ≥59 (480) | ≥18 (180) | ||||
| EN | 1.4301 | (500-700) | ≥20 (195) | ≥40 | 1000ºC-1100ºC Water Quenching | |
| 1.4307 | (470-670) | ≥18 (180) | ||||
| 1.4401 | (510-710) | ≥21 (205) | 1020ºC-1120ºC Water Quenching | |||
| 1.4404 | (490-690) | ≥19 (195) | ||||
| Stainless Steel Heat Exchanger Tube | ||||
| Standard | OD(mm) | WT(mm) | Length(meters) | Grade |
| ASTM A249, ASTM A269, EN 10217-7 | 15.88 to 114.3 | 0.3 to 4.0 | Up to 18.3 meter | 1.4301, 1.4306, 1.4404, AISI 304/304l/316l, S31803/S32205, etc |
| Standard | Outside Diameter | Thickness | Length | |
| ASTM A249 (A1016) | <25.4 | ±0.10 | ±10%S | OD<50.8+3-0 OD≥50.8+5-0 |
| ≥25.4~<38.1 | ±0.15 | |||
| ≥38.1~<50.8 | ±0.20 | |||
| ≥50.8~<63.5 | ±0.25 | |||
| ≥63.5~<76.2 | ±0.31 | |||
| ASTM A269 (A1016) | <38.1 | ±0.13 | OD<12.7±15% OD≥12.7±10% | OD<38.1+3.2-0 OD≥38.1+4.8-0 |
| ≥38.1~<88.9 | ±0.25 | |||
| ≥88.9~<139.7 | ±0.38 | |||
| Chemical Composition | Tensile Strength | Yield Strength | Elongation | Hardness HRB |
| Grade 304 Stainless Steel (100% & MPA) | ||||
| C≤0.08, Mn≤2, P≤0.045, S≤0.03, Si≤0.75, 8≤Ni≤10.5, 18≤Cr≤20 | ≥515 | ≥205 | ≥40 | ≤92 |
| Grade 304L Stainless Steel (100% & MPA) | ||||
| C≤0.03, Mn≤2, P≤0.045, S≤0.03, Si≤0.75, 8≤Ni≤12, 18≤Cr≤20 | ≥485 | ≥170 | ≥40 | ≤92 |
| Grade 316L Stainless Steel (100% & MPA) | ||||
| C≤0.03, Mn≤2, P≤0.045, S≤0.03, Si≤0.75, 10≤Ni≤14, 16≤Cr≤18 | ≥485 | ≥170 | ≥40 | ≤95 |
The 10Cr17Ni13Mo2Ti stainless steel tubes for boiler application pictures:
Tags:10Cr17Ni13Mo2Ti stainless steel pipes,GOST9941-1981 stainless steel tubes,316Ti stainless,